Полифениленсульфид — новый функциональный инженерный пластик.

What is PPS? PPS has a symmetrical rigid backbone and is part of a crystalline polymer consisting of repeated parapplacement of benzene rings and sulfur atoms. PPS are special engineering plastics with high performance, high melting point up to 280℃, which can replace metal. They are located at the top of the polymer property pyramid, as shown in Figure 1. Therefore, based on the excellent performance of PPS resin, make it meet the requirements of harsh engineering plastic projects for materials. Why filling long glass fiber? Long glass fiber reinforced plastic is on the basis of the original pure plastic, adding glass fiber and other additives, so as to improve the scope of use of materials. Advantages: 1. After glass fiber reinforcement, glass fiber is a high temperature resistant material, therefore, the heat resistance temperature of reinforced plastics is much higher than before without glass fiber, especially nylon plastics; 2. After glass fiber reinforcement, due to the addition of glass fiber, limited the mutual movement between polymer chains of plastics, therefore, the shrinkage rate of reinforced plastics decreases a lot, rigidity is greatly improved; 3. After glass fiber reinforcement, the reinforced plastic will not stress crack, at the same time, the anti-impact performance of plastic is improved a lot; 4. After glass fiber reinforcement, glass fiber is a high strength material, which also greatly improves the strength of plastic, such as: tensile strength, compression strength, bending strength, improve a lot; 5. glass fiber reinforced after, due to the addition of glass fiber and other additives, the combustion performance of reinforced plastics decreased a lot, most of the material can not ignite, is a kind of flame retardant material. Datasheets for your reference К эксплуатационным преимуществам относятся следующие аспекты: превосходная термостойкость, хорошие механические свойства, коррозионная стойкость, самовоспламеняемость до уровня UL94 V-0. Поскольку PPS обладает преимуществами вышеперечисленных свойств и по сравнению с другими термопластичными конструкционными пластиками с высокими эксплуатационными характеристиками, а также отличается простотой обработки и низкой стоимостью, он становится отличной смоляной матрицей для производства композитных материалов. Подробности Цвет Оригинал или по мере необходимости Длина Выше 5 ~ 24 мм Минимальный заказ 25 кг Упаковка 25 кг мешок Порт погрузки Порт Сямэнь Срок поставки 7~15 дней после отгрузки

Что такое ППС? Полифениленсульфид (PPS) — новая термопластичная смола с высокими эксплуатационными характеристиками. Путем наполнения, модифицированного с превосходной термостойкостью, коррозионной стойкостью, износостойкостью, огнестойкостью, сбалансированными физико-механическими свойствами и отличной размерной стабильностью, отличными электрическими свойствами и другими характеристиками новой термопластичной смолы с высокими эксплуатационными характеристиками, а также высокой механической прочностью, химическая стойкость, огнестойкость, хорошая термическая стабильность, отличные электрические свойства и другие преимущества. Он обладает такими преимуществами, как твердость и хрупкость, высокая кристалличность, воспламеняемость, хорошая термическая стабильность, высокая механическая прочность, отличные электрические свойства, сильная химическая коррозионная стойкость и так далее. Механические свойства чистого ППС невысокие, особенно ударная вязкость относительно низкая. Хорошее сопротивление ползучести под нагрузкой, высокая твердость; Высокая износостойкость, износ при 1000 об/мин составляет всего 0,04 г, и будет дополнительно улучшен после заполнения F4 и дисульфидом молибдена; Он также имеет определенную степень самоувлажнения. Механические свойства ПФС менее чувствительны к температуре. Что такое ППС-ЛГФ? PPS является одним из лучших вариантов термостойкости в отделе инженерных пластиков. Температура термической деформации материала, модифицированного стекловолокном, обычно превышает 260 градусов, а химическая стойкость уступает только ПТФЭ. Кроме того, он также имеет небольшую усадку, низкое водопоглощение, хорошую огнестойкость. Хорошая устойчивость к вибрационной усталости, высокая устойчивость к дуге, особенно при высокой температуре. Отличная электроизоляция при высокой влажности. Но его недостатками являются хрупкость, ударная вязкость, низкая ударная вязкость, после модификации можно преодолеть вышеуказанные недостатки, получить очень отличные комплексные характеристики. Как пластик, его свойства и использование намного превосходят свойства обычного пластика, и во многих отношениях он не уступает металлическим материалам. Excellent material PPS has the advantages of high temperature corrosion resistance, excellent mechanical properties, can replace metal including stainless steel, copper, aluminum, alloy, etc., is considered to be the best substitute for metal, copper. What is the application of PPS-LGF? PPS is now widely used in automotive, aerospace, household appliances, mechanical construction and chemical industry for a variety of structural parts, transmission parts, insulation parts, corrosion resistant parts and seals. Under the condition of ensuring sufficient strength and other properties, the weight of the product is greatly reduced. Datasheet for reference Details Number Color Length MOQ Package Sample Delivery time Port of Loading PPS-NA-LGF30 Original color (can be customized) 5-25mm above 25kg 25kg/bag Available 7-15 days after shipment Xiamen Poer Production process Trademarks and patents Teams and customers We will offer you: 1. LFT & LFRT material tec

PPS-LCF materials Polyphenylene sulfide (PPS) is a linear semi-crystalline polymer with benzene ring and sulfur atoms composed of molecular main chain, its melting point is about 280℃, and has many excellent characteristics, with a series of excellent properties, such as excellent mechanical properties, chemical stability, solvent resistance, flame retardant, and has good processing and molding properties. As a kind of special engineering plastic with the largest output at present, the market application foundation is mature. In addition, in the molding process, pultrusion molding, injection molding, molding and other methods can be processed. By reinforcing PPS resin with carbon fiber, excellent mechanical properties and heat resistance composites can be prepared. At present, PPS fiber reinforced composites have been widely used in the aerospace field. Tencate Company of the United States uses PPS resin of Fortron brand of Ticona company of Germany to produce carbon fiber /PPS composites based on fabric hot pressing molding method. The material is used in Airbus A340 and A380 aircraft wing main edge, A340 aircraft aileron structure, Fokker50 aircraft landing gear door stress rib and girder, G650 business aircraft tail, rudder and elevator components. Advantages Performance characteristics: ◊ receiving aerospace OEM specifications and receiving certification; ◊ excellent cost performance; ◊ Working temperature exceeding Tg according to the design requirements on parts; ◊ laminates can protect against lightning strike and electrochemical corrosion. ◊ inherent flame retardant ◊ excellent chemical stability and solvent resistance; ◊ Long-term storage at ambient temperature. Main applications: ◊ Major and minor aircraft structures: ◊ wing leading edge, engine tower, body splint structure, etc. ◊ aircraft interior structure: ◊ seat structure parts, trunk, etc ◊ On specific requirements on corrosion resistance, dimensional stability, and shock absorption on high-end industrial areas Application Производственный процесс Наша команда и клиенты Приходите и свяжитесь с нами!

PPS The molecular structure of PPS consists of benzene ring and sulfur atoms interarranged, the configuration is orderly, easy to form a high thermal stability of the crystal structure. At the same time, the molecular structure of PPS material has a highly stable chemical bond characteristics, the benzene ring structure makes PPS more rigid, and the sulfur ether bond (-S-) provides a certain degree of flexibility. PPS itself has good heat resistance, flame retardant, chemical resistance, should be a promising material, but unmodified PPS has some unavoidable defects: Difficult processing:  This is the biggest pain point of all high temperature resistant materials -- high processing temperature, no matter the molding process or processing energy consumption, will face great challenges. In addition, PPS is still prone to thermal oxidation crosslinking in the melting process, resulting in reduced fluidity and further improve the processing difficulty; Poor toughness: PPS molecular chain is rigid, the maximum crystallinity is as high as 70%, the elongation is low and the welding strength is not so good. As a result, the impact resistance of unmodified PPS is poor, which limits the application scope. High cost: PPS raw materials and general engineering plastics compared, the price is about 1-2 times higher, and some modified materials compared with low cost performance; Difficult coating: PPS surface coating and coloring performance is not ideal. While this is not a major problem for now, it is a limiting factor. PPS-LGF Long glass fiber reinforced composites can solve your problems when other methods of reinforced plastics do not provide the performance you need or if you want to replace metal with plastic. Long glass fiber reinforced composites can cost-effectively reduce the cost of goods and effectively improve the mechanical properties of engineering polymers, and increase the durability by forming long fibers to form a long-fiber-reinforced internal skeleton network. Performance is preserved in a wide range of environments. TDS для справки Приложение О нас Композитный пластик Xiamen LFT Co., Ltd. является фирменной компанией, специализирующейся на LFT и LFRT. Серия длинного стекловолокна (LGF) и серия длинного углеродного волокна (LCF). Термопласт LFT можно использовать для литья под давлением и экструзии LFT-G, а также для литья LFT-D. Он может быть изготовлен в соответствии с требованиями заказчика: длина 5 ~ 25 мм. Длинноволокнистые армированные термопласты компании с непрерывной инфильтрацией прошли системную сертификацию ISO9001 и 16949, а продукция получила множество национальных товарных знаков и патентов.

PPS Special engineering plastics are engineering plastics with higher overall performance and long-term use temperature above 150℃, PPS is one of them. The carbon fiber reinforced special engineering composites formed by carbon fiber as the reinforcement and these special engineering plastics as the matrix have excellent mechanical properties, wear resistance and high temperature resistance, which can be used in aerospace, marine or medical fields, and in some aspects show more desirable application advantages than thermosetting resins or even metal materials. PPS-LCF Polyphenylene sulfide PPS resin strength and hardness are relatively high, good mechanical properties, adapt to a variety of molding and processing methods, you can achieve secondary precision molding, the dimensional stability of the product is better. Its moisture absorption rate of only 0.03%, low density, melt temperature Tm of 285 ℃, the glass transition temperature Tg of 90 ℃, thermal stability is very good, in the air state, to reach 430 ℃ -460 ℃ before decomposition, high flame retardant grade, 200 ℃ insoluble in most organic solvents, excellent electrical insulation. As a special engineering plastics, PPS advantages are outstanding, but defects also exist, for example, because of the large number of benzene ring to make its impact resistance and elongation is not good enough, but through the carbon fiber reinforced way, can further improve the performance of the material strength and thermal stability, so as to better show the value of the application of the material. Through the carbon fiber reinforced intervention, changing the original insulating properties of PPS into a conductive, anti-static properties, polyphenylene sulfide PPS toughness and strength can be substantially increased and improved, becoming one of the most commonly used composite materials in the aerospace field. It is used in aircraft landing gear, wings, hatches, fuel tank port covers, J-shaped nose cone, cabin interior trim and other components, not only to help increase the impact resistance, high temperature and corrosion resistance of these parts, more through the reduction in mass, to enhance the aircraft load efficiency and reduce fuel consumption. Compared with metal, this composite material has the advantages of low cost and easy processing, the cost can be reduced by 20-50 percent. High bonding must be maintained between the carbon fiber reinforcement and the PPS resin matrix. When the product is subjected to stress, this high bonding helps the interface to transfer the external load to the fibers effectively, which can effectively prevent cracks from debonding between the interfaces, in addition to enhancing the mechanical properties of the composite. To make the resin matrix and carbon fiber reinforcement between the formation of high bonding, we must make the molten state of PPS resin and carbon fiber reinforcement in full contact, full impregnation, so that the fiber body in the case of uniform dispersion to achieve good impregnation effect. Production process Application of PPS-LCF Xiamen LFT composite plastic Co., Ltd We will offer you: 1. LFT & LFRT material technical parameters and leading edge design 2. Дизайн передней части пресс-формы и рекомендации 3. Обеспечьте техническую поддержку, такую ​​как литье под давлением и литье под давлением. О нас

Polyphenylene sulfide PPS is one of the typical representatives of special engineering plastics, with a linear structure of alternating benzene rings and sulfur atoms. In the condensed structure, PPS is easy to crystallize, crystallinity of nearly 70%, therefore, has good thermal stability, chemical stability and dimensional stability, etc. PPS mainly has the following five performance advantages. (1) excellent heat resistance. pps melting point of more than 280 ℃, heat deflection temperature of more than 260 ℃, and after high-temperature heat aging treatment, the strength retention rate is high. (2) since the flame retardant. PPS itself has flame retardant, without adding flame retardants flame retardant level can reach UL94 V- 0 level. (3) good mechanical properties. PPS is a brittle material, has good creep resistance, high surface hardness, good wear resistance, and carbon fiber and other materials compound, but also shows good self-lubricating properties. (4) excellent chemical resistance, irradiation resistance. pps below 200 ℃ almost insoluble in any solvent, can withstand almost all inorganic substances, radiation dose up to 108Gy. (5) good processing properties. pps melt viscosity is low, as the resin matrix of composite materials, for the reinforcement of the flow of excellent wetting effect. As PPS has the above performance advantages, and compared to other high-performance thermoplastic resins and easy processing, low cost, so become an excellent resin matrix for the manufacture of composite materials. Long glass fiber Glass fiber is an inorganic non-metallic material with excellent performance, is a natural mineral with silica as the main raw material, add specific metal oxide mineral raw materials, mixed evenly, molten at high temperature, molten glass liquid flow through the funnel outflow, in the role of high-speed pull gravitational force is drawn and rapidly cooled and cured into a very fine continuous fiber. Glass fiber monofilament diameter from a few microns to more than twenty microns, equivalent to a hair of 1/20-1/5, each bundle of fiber original filament are composed of hundreds or even thousands of monofilaments. Glass fiber basic properties: The appearance of a smooth cylindrical surface, the cross-section is a complete circle, round cross-section to withstand the load capacity; gas and liquid through the resistance is small, but the surface is smooth so that the holding force of the fiber is small, not conducive to the combination with the resin; density is generally in 2.50-2.70 g/cm3, depending mainly on the glass composition; tensile strength than other natural fibers, synthetic fibers to be high; brittle materials, the elongation at break is very small ; water resistance and acid resistance is good, while alkali resistance is poor. It can be divided into continuous glass fiber, short glass fiber (SGF) and long glass fiber (LGF) by length classification. Long glass fiber is the most widely used glass fiber at present. And Xiamen LFT plastic composite company is focuses on the produce of long glass fiber compounds for many years. SGF VS LGF 1. Разница в длине инженерных материалов длинного стекловолокна и короткого стекловолокна буквально означает разницу в длине; более распространенный размер короткого стекловолокна составляет около 0,2–0,6 мм между ними; размер длинного стекловолокна составляет около 6-25 мм между ними. 2. Различия в силе производительности Различные длины стекловолокна отличаются по своей прочности, длина волокна длинных стекловолокон в композиционном материале внутри ударной вязкости, чем короткие стекловолокна сильнее. 3. Производственный процесс отличается Производство длинного стекловолокна, высокие требования к сырью, особенно производственный процесс требует активации поверхности стекловолокна, обработка не может быть залита стекловолокном, а также происходит явление внешней утечки. Производство короткого стекловолокна, потому что к размеру, как правило, нет особых требований, поэтому производство относительно простое, требования к сырью не так высоки, производственные затраты для производителей низкие. 4.

Информация о PPS Полифениленсульфид (PPS) не улучшается перед модификацией, его недостатками являются хрупкость, плохая ударная вязкость, низкая ударная вязкость, после заполнения стекловолокном, углеродным волокном и другими модификациями, модифицированными для преодоления вышеуказанных недостатков, для получения очень хороших общих характеристик. Наполнение PPS Длинное углеродное волокно В индустрии модифицированных инженерных пластмасс композиты, армированные длинным волокном, представляют собой композиты, изготовленные из длинных углеродных волокон, длинных стеклянных волокон и полимерной матрицы с помощью ряда специальных методов модификации. Наиболее важной особенностью композитов с длинными волокнами является то, что они обладают превосходными характеристиками, которых нет у исходных материалов. Если классифицировать их по длине добавляемых армирующих материалов, то их можно разделить на: длинноволокнистые, коротковолокнистые и непрерывные волокнистые композиты. Композиты из длинного углеродного волокна представляют собой один из видов композитов, армированных длинным волокном, которые представляют собой новый волокнистый материал с высокой прочностью и высоким модулем. Это новый материал с отличными механическими свойствами и множеством специальных функций. Коррозионная стойкость: композитные материалы LCF из углеродного волокна обладают хорошей коррозионной стойкостью и могут адаптироваться к суровым условиям работы. Стойкость к УФ-излучению: способность противостоять УФ-излучению высока, и продукты меньше повреждаются УФ-излучением. Устойчивость к истиранию и ударам: преимущество по сравнению с обычными материалами более очевидно. Низкая плотность: более низкая плотность, чем у многих металлических материалов, позволяет достичь легкого веса. Другие свойства: такие как уменьшение коробления, повышение жесткости, модификация удара, повышение ударной вязкости, электропроводности и т. д. Композиты из углеродного волокна LCF имеют более высокую прочность, более высокую жесткость, меньший вес и отличную электропроводность по сравнению со стекловолокном. PPS TDS для справки Приложение PPS Другие продукты вы также можете связаться с нами для получения дополнительной технической консультации. вопросы и ответы 1. Являются ли композитные изделия из углеродного волокна очень дорогими? Цена композитных изделий из углеродного волокна тесно связана с ценой на сырье, уровнем технологии и количеством изделий. Чем выше характеристики исходного материала, тем он дороже, например, термопластический материал из углеродного волокна PEEK, используемый в ортопедии. Конечно, чем сложнее производственный процесс, тем больше рабочее время и нагрузка, а также возрастают произво

материал ППС В последние годы применение специальных инженерных пластиков постепенно расширилось от прежних военных и аэрокосмических областей до все большего числа гражданских областей, таких как автомобилестроение, производство оборудования, потребительские товары высокого класса и т. Д. Среди них полифениленсульфид (PPS). ) и полиэфирэфиркетон (PEEK) — это два специальных конструкционных пластика, которые относительно быстро разрабатывались и имеют широкий спектр применения. PEEK превосходит PPS с точки зрения прочности, ударной вязкости и максимальной рабочей температуры. Что касается стойкости к высоким температурам, PEEK примерно на 50°C выше, чем PPS. Но, с другой стороны, относительно очевидные ценовые преимущества и лучшие технологические свойства ПФС делают его более широко используемым. PPS представляет собой кристаллический, очень жесткий белый порошкообразный полимер, обладающий высокой термостойкостью (длительное использование 200 ℃ -220 ℃, кратковременное выдерживает высокие температуры 260 ℃), механическая прочность, жесткость, огнестойкость, химическая стойкость. , электрические свойства, стабильность размеров - отличные смолы. Обладает отличной износостойкостью, сопротивлением ползучести, огнестойкостью и самозатухающими свойствами. Он сохраняет хорошие электрические свойства при высокой температуре и высокой влажности. Хорошая сыпучесть, легко формуется, практически не дает усадки и вогнутости при формовании. Хорошее сродство с различными неорганическими наполнителями. Он был разработан, чтобы сократить разницу между стандартными термопластическими материалами (например, PA, POM, PET ......) и передовыми конструкционными пластиками. PPS имеет следующие явные преимущества производительности: (1) Внутренняя огнестойкость В отличие от поликарбоната и полиамида, чистая смола PPS и композиты, наполненные стекловолокном/минеральным порошком, не содержат каких-либо добавленных антипиренов. Хотя ПК и ПА имеют более низкую цену и лучшую механическую прочность (особенно ударную вязкость), чем ППС, стоимость композитов ПК и ПА с добавлением безгалогенных антипиреновых составов (V-0@0,8 мм²) значительно выше, во многих случаях даже выше, чем у материалов PPS с такой же механической прочностью. (2) Сверхвысокая текучесть Для полукристаллического ПФС его очень высокая текучесть позволяет легко заполнять стекловолокно более чем на 50%, в то время как в процессе высокотемпературной экструзии смешивания расплава ПФС с более низкой вязкостью по сравнению с поликарбонатом может заставить стекловолокно выдерживать более низкую температуру. сдвига и экструзии, так что конечные продукты, полученные литьем под давлением, имеют более длительный срок удерживания, чтобы еще больше усилить эффект модуля. (3) Сверхнизкое водопоглощение Это преимущество в основном для PA. С точки зрения текучести высоконаполненный ПА и ПФС сопоставимы; а по механическим свойствам такое же количество наполнителя ПА композитов будет более выгодным. Но в дополнение к ограничениям огнестойкости без галогенов, еще одним фактором, ограничивающим применение ПА, является его высокое водопоглощение: по сравнению с высокотемпературным нейлоном PA6T с водопоглощением 0,6–1%, водопоглощение PPS 0,03% практически незначительно. В результате продукты PPS из-за водопоглощения и деформации дефекта продукта намного ниже, чем те же условия продуктов PA. (4) уникальная металлическая текстура и более высокая твердость поверхности Детали, отлитые под давлением из PPS, будут падать на стол, и это будет очень четкий звук, уникальный для PPS. Благодаря специальной пресс-форме и разумной температуре пресс-формы детали, отлитые под давлением из PPS, на ощупь также будут звучать так же, как удар металла, поверхность будет гладкой, как зеркало, с металлическим блеском. Соединения PPS-LCF Длина: около 12 мм или по индивидуальному заказу Цвет: исходный цвет или индивидуальный Спецификация волокна: 20%-60% Оценка: Общая оценка Композиты, армированные длинным углеродным волокном, обеспечивают значительную экономию веса и обеспечивают оптимальные свойства прочности и жесткости в армированных термопластах. Превосходные механические свойства композитов, армированных длинным углеродным волокном, делают их идеальной заменой металлам. В сочетании с конструкционными и производственными преимуществами термопластов, полученных литьем под давлением, композиты с длинным углеродным волокном упрощают переосмысление компонентов и оборудования с высокими требованиями к производительности. Его широкое использование в аэрокосмической и других передовых отраслях промышленности делает его «высокотехнологичным» для потребителей. Технический паспорт для справки Приложение Фабрика Вопросы и ответы 1. Существуют ли единые справочные данные о характеристиках изделий из углеродного волокна? Характеристики определенных нитей из углеродного волокна фиксированы, например нити из углеродного волокна Toray, T300, T300J, T400, T700 и т. д. Существует ряд параметров, которые можно отследить. Тем ...

Наполнитель полиамид 12 длинное стекловолокно Рекомендуемая длительная рабочая температура полифениленсульфидной смолы (PPS) составляет 220~240℃. Материал обладает хорошей термической стабильностью, а его механические свойства остаются на уровне около 80% и 60% от исходных значений при 100°С, 160°С и 200°С соответственно. Материал обладает превосходным сопротивлением ползучести и сопротивлением усталости при комнатной температуре. Материал также обладает отличной стойкостью к кислотам, щелочам, солям, органическим растворителям и другим средам, за исключением окисляющих кислот и сильных окислителей, и практически нерастворим в любом химическом растворителе при температуре ниже 170°C. Он особенно подходит для плавиковой кислоты, галогенированных углеводородов и коррозионной стойкости к ионам хлора. ПФС — огнестойкий материал с кислородным индексом от 46 до 53, лучше, чем у большинства инженерных пластиков. Полифениленсульфид обладает высоким сопротивлением и низкими электрическими свойствами диэлектрической проницаемости и может сохранять хорошие электрические свойства в условиях высокой температуры и высокой влажности. Кроме того, механические свойства полимерного материала не очень выдающиеся, поскольку он имеет хорошее сродство со стекловолокном, углеродным волокном, неорганическим наполнителем и твердой смазкой, а модификация является хорошей, поэтому частицы, используемые при литье под давлением, в основном модифицируются и армируются. различными волокнами и неорганическими наполнителями. LGF и SGF Частицы нейлона из обычного стекловолокна: Размер составляет около 3-4 мм, отношение длины к ширине 50-250. Длинные частицы нейлона из стекловолокна: Размер составляет около 10-12 мм, соотношение сторон > 400. Кроме того, распределение стекловолокна по двум виды частиц также различны. По сравнению с SGF, LGF обладает повышенной жесткостью, прочностью и модулем упругости, особенно значительно улучшены ударные характеристики с надрезами. По сравнению с SGF, LGF обладает повышенной жесткостью, прочностью и модулем упругости, особенно значительно улучшены ударные характеристики с надрезами. Скорость сохранения жесткости длинного стекловолокна лучше, чем у короткого стекловолокна, а длинное стекловолокно более устойчиво к тепловому старению. На характеристики ползучести влияют время, температура и нагрузка. При температуре 120 ℃ и нагрузке 40 МПа ползучесть длинного стекловолокна значительно лучше, чем у короткого стекловолокна. Это имеет решающее значение для деталей с длительным статическим давлением, и можно попробовать длинное стекловолокно, когда короткое стекловолокно не соответствует требованиям. Усадка имеет решающее значение для размера детали. Поперечная усадка материала из коро�